Los dientes artificiales son una de las aplicaciones de las resinas acrilicas en odontologia. Sus propiedades dependen de la tecnica utilizada para manipular la resina acrilica termocurable durante su fabricacion. Diversa literatura en torno a las resinas acrilicas para base de protesis reportan la dependencia de la porosidad y la dureza en algunos parametros de la tecnica de fabricacion como la presion, la temperatura y la proporcion polvo-liquido. En el caso de los dientes acrilicos son pocos los estudios reportados y se desconoce su efecto. En este proyecto, se modificaron dos parametros de la tecnica de fabricacion de los dientes acrilicos: la temperatura y la proporcion polvo-liquido, para analizar su efecto sobre la dureza y porosidad. La dureza se midio empleando el indentador Knoop y la porosidad se analizo en un microcopio electronico de barrido (SEM). Se encontro que la temperatura es la variable que mas afecta la dureza y que ninguna modificacion de las dos variables genera porosidad interna en la resina acrilica. Todos los procedimientos se llevaron a cabo siguiendo la Norma Tecnica Colombiana 1591: Dientes de Resinas Acrilicas. ABSTRACT. Artificial teeth is one of the most common applications of acrylic resins in Dentistry. The technique used by the manufacturers to handle the heat curing resin affects the final product properties. Several studies about acrylic resins for denture base materials have reported that when some parameters of the manufacturing technique are changed, for example the pressure, the temperature, and the powder-liquid ratio; the porosity and hardness are affected. However, in the case of acrylic teeth the effect is unknown. In this project, two parameters of the manufacturing process of artificial teeth were modified: temperature and powder-liquid ratio, and its effect on the hardness and porosity were analyzed. For measuring hardness a Knoop indenter was used, and for analyzing the porosity the Scanning Electron Microscope (SEM) technique. It was found that temperature is the variable that affects the most superficial hardness and that none of the studied variables generated internal porosity when they were modified. All the procedures were made according to Norma Tecnica Colombiana 1591: Dientes de Resinas Acrilicas.