RESUMEN Por medio de las tecnicas Resistencia a la Polarizacion Lineal, Espectroscopia de Impedancia Electroquimica y Extrapolacion de Tafel, se evaluo la corrosion del acero API 5L grado X65 con un Electrodo de Cilindro Rotatorio (ECR), en una solucion desaireada al 3% en peso de NaCl a 40 oC y a presion atmosferica. La dinamica de las pruebas fue controlada por el ECR con velocidades entre 0 y 3m/s, variando la concentracion de la relacion molar H2S/CO2, desde 0 a 8.34x10-3. Se calcularon los coeficientes de transferencia de masa de las especies H+, HS- y HCO3- y los esfuerzos de corte cerca de la interfase metal–liquido, empleando correlaciones experimentales aplicables para la geometria del ECR. Finalmente, se determino la relacion entre la velocidad de corrosion, los coeficientes de transferencia de masa y los esfuerzos de corte, con la velocidad de flujo de este sistema multifasico y la relacion molar H2S/CO2. PALABRAS CLAVE: Corrosion tipo meseta, Velocidad de corrosion, ECR, Sistema multifasico CO2–H2S-salmuera. ABSTRACT By using Linear Polarization Resistance, Electrochemical Impedance Spectroscopy and Tafel Extrapolation, the corrosion resistance of a carbon steel API 5L X65 degree was evaluated in the Rotating Cylinder Electrode (RCE), submerged in a 3%p NaCl solution deareated and 40 oC at atmospheric pressure. The dynamics of tests was controlled by the RCE with speeds between 0 and 3 m/s, and varying the H2S/CO2 molar relation from 0 to 8.34x10-3. The mass transference coefficients of H+, HS- and HCO3- and the shear stress near the interface metal-liquid interface were determined, by using applicable experimental correlations for the geometry of RCE. Finally, correlations were determined which showed the relationship between the corrosion rate and the mass transference coefficients and shear stress, with the fluid flow of this multiphase system and the H2S/CO2 molar ratio. KEY WORDS: Corrosion type plateau, corrosion rate, ERC, CO2- H2S- brine multiphase system.