Photocatalytic activity of white Portland cement paste samples, added with 0.5, 1.0 and 3.0% wt of titanium dioxide nanoparticles, was evaluated trough the degradation of Rhodamine B. The degradation was measured by the change of the color coordinates CIE L*a*b* of samples exposed to a UV source and a photocatalytic efficiency coefficient, ξ, was calculated for two times of curing (65h and 28d). Three ratios of anatase:rutile were used (100:0, 85:15, 50,50) for each percentage of addition. Results showed that samples with the highest photocatalytic activity correspond to 3.0% of anatase at early ages, and 3.0% of anatase:rutile (50:50) at late ages. La actividad fotocatalitica de pastas de cemento Portland blanco, adicionadas con 0,5%, 1,0% y 3,0% en peso de nanoparticulas de dioxido de titanio, fue evaluada a traves de la degradacion de Rodamina B. La degradacion fue medida en funcion del cambio en las coordenadas de color CIE L*a*b* de las muestras expuestas a un fuente ultravioleta, UV, y un coeficiente fotocatalitico, ξ, fue calculado para dos edades de curado (65 horas y 28 dias). Tres proporciones de anatasa:rutilo fueron empleadas (100:0, 85:15, 50:50) para cada porcentaje de adicion. Los resultados mostraron que las muestras con la mayor actividad fotocatalitica correspondieron a un 3,0% de anatasa a edades tempranas y un 3,0% de anatasa:rutilo (50:50) a edades tardias.