Se desarrollaron biorecubrimientos de TiO 2 e hidroxiapatita (HA) dopada con magnesio (TiO 2 /HA-Mg) sobre acero inoxidable AISI 316L por la tecnica dip-coating, a partir de suspensiones de polvos de HA-Mg (obtenidos por tratamiento hidrotermal de hueso bovino en soluciones de Mg(NO 3 ) 2 ) en soles de TiO 2 . Los polvos de hidroxiapatita biologica dopada con Mg fueron caracterizados por las tecnicas analiticas de DRX y FT-IR, con el fin de evaluar los cambios composicionales. Por su parte, las caracteristicas de los recubrimientos se evaluaron mediante microscopias optica y electronica de barrido, fuerza de adherencia al sustrato, bioactividad in vitro en SBF y resistencia a la corrosion. El tratamiento hidrotermal del hueso bovino permitio obtener hidroxiapatita de mayor reactividad gracias a su dopaje con Mg, lo que fue confirmado mediante la caracterizacion electroquimica de las peliculas. La modificacion de la HA con Mg no afecta en mayor medida las propiedades fisico-mecanicas de las peliculas de TiO 2 /HA. El incremento en la bioactividad de la HA solo se observo al modificarla con un 10% de Mg, de modo que durante la inmersion de este recubrimiento en SBF presenta una etapa inicial de disolucion del biomaterial y la posterior formacion de apatitas sobre su superficie. Bio-coatings of TiO 2 and biological hydroxyapatite (HA) doped with magnesium (TiO 2 /HA-Mg) were deposited on AISI 316L stainless steel by dip-coating technique, from suspensions of HA-Mg powders (which were obtained by hydrothermal treatment of bovine bone in solutions of Mg(NO 3 ) 2 ) in TiO 2 sols. Biological hydroxyapatite powders doped with Mg were characterized by XRD and FT-IR analytical techniques, in order to evaluate the compositional changes. On the other hand, the coating’s characteristics were evaluated by scanning electron and optic microscopies, adhesion force to the substrate, in vitro bioactivity in SBF and corrosion resistance. The bovine bone hydrothermally treated allowed to obtain hydroxyapatite with greater reactivity due to its doping with Mg, what was confirmed throughout the electrochemical characterization of the films. The modification of HA with Mg does not significantly affect the physical and mechanical properties of the TiO 2 /HA films. An increment in the bioactivity of the HA was only observed when it was modified with 10% Mg, so that during the immersion of this coating in SBF shows an initial stage of biomaterial dissolution and the subsequent stage of apatites formation on its surface.