Resumen En el presente articulo se presenta un estudio de la cinetica de formacion del poliuretano producido a partir de aceite de ricino e isoforona diisocianato. La velocidad de reaccion fue monitoreada por calorimetria diferencial de barrido (DSC). Se evaluaron comparativamente tres modelos de reaccion con sus correspondientes ecuaciones de velocidad de reaccion para representar el comportamiento de los datos experimentales. El modelo de orden n y el modelo de autocatalisis fueron descartados por inconsistencias con las bases de la ecuacion de Arrhenius y por bajo indice de correlacion de datos. Se propone un modelo de reaccion que considera los efectos quimicos y fisicos (difusion) presentes en la reaccion de un monomero poli funcional como es el caso objeto del presente estudio. Este modelo permite un buen ajuste de los datos experimentales de velocidad de reaccion. Se aplicaron metodos de isoconversion y regresion no lineal para el calculo de los parametros cineticos. Se realizo un analisis comparativo de la magnitud de las resistencias y se encontro que la difusion es la mayor resistencia a la reaccion en casi todo el intervalo de conversion. Palabras clave: cinetica, poliuretano, aceite de ricino, resistencia por difusion, resistencia quimica, DSC. Kinetic study of polyuretane syntesis produced from castor oil using Differential Scanning Calorimetry Abstract This paper presents a study of the kinetics of polyurethane formation produced from castor oil and isophorone diisocyanate. The reaction rate was monitored by means of Differential Scanning Calorimetry (DSC). Three reaction models with their respective reaction rates were evaluated by comparison in representing experimental data of reaction rate. The model of order n and the auto catalytic were discharged for inconsistency with the bases of Arrhenius equation and for poor correlation with experimental data. A reaction model is proposed considering two resistances to reaction due to chemical and physical effects (diffusion) present in the polymerization of a poly functional monomer as in the case under study. This model faithfully represents the experimental data of reaction rate. Iso-conversion and nonlinear regression techniques were applied to calculate the kinetic parameters. A comparative analysis of the magnitude of the resistances allowed fnding that diffusion is the major resistance during most of the conversion interval. Keywords: kinetics, polyurethane, castor oil, diffusion resistance, chemical resistance, DSC.