Teniendo en cuenta los problemas ambientales asociados con la produccion del Cemento Portland (CP), en los ultimos anos se ha promovido el uso de la Ceniza Volante (CV) en la produccion de concretos. La utilizacion de la CV se ha dado principalmente mediante su activacion con el CP y como material cementante geopolimerico. En este articulo una tercera tecnica de activacion de la CV conocida como electrometagenesis es investigada. Esta consiste en la activacion de la CV, a partir del ingreso de iones de una solucion alcalina mediante la aplicacion de un campo electrico a traves del concreto endurecido. Como fuente de iones alcalinos se usaron soluciones de hidroxido de sodio/silicato de sodio con varias relaciones molares. Una vez terminado el tratamiento se evaluo la variacion en la resistencia a la compresion, la velocidad de pulso ultrasonico y la microestructura de la matriz del concreto. Los resultados mostraron que los iones alcalinos migrados dentro del concreto reaccionaron con las particulas de CV mutando estas a nuevas fases, produciendo un aumento en sus propiedades. Taking into account the environmental problems associated with the production of Portland cement (PC), in recent years the use of Fly Ash (FA) in the production of concrete has been promoted. The use of fly ash has been possible through the activation with Portland cement and as a geopolymeric cementitious material. In this paper, a third activation technique for fly ash, known as electrometagenesis, was investigated. This treatment consists in the activation of fly ash after the migration of ions from an external alkaline solution, by applying an electric field across the hardened concrete. As a source of alkaline ions, solutions of sodium hydroxide and sodium silicate with various molar ratios were used. After finishing the treatment, the variation in the compressive strength, the ultrasound pulse, and the microstructure of concrete matrix were evaluated. Results showed that the alkaline ions migrated into the concrete matrix, reacted with fly ash, and mutated in new phases, producing an improvement in their physical properties.