Abstract Cellulose nanofibers were obtained from the Colombian fique ( Furcraea bedinghausii ) and Acrylic hydrogels (H) and reinforced acrylic hydrogels with fique nanofibres (HRFN) were synthesized, using the solution polymerization method. The extraction was carried out using a combined extraction method (chemical procedures and ultrasound radiation). The raw material (NAT-F), bleached fibers (B-F), hydrolyzed fibers and fibers treated with ultrasound (US-F) were characterized by infrared spectroscopy (FTIR) and thermal stability analysis; also, in order to have a comparison criterion, a commercial microcrystalline cellulose sample (CC) was analyzed, which demonstrated the extraction of fique cellulose. The surface morphology of the NAT-F and the B-F was determined by scanning electron microscopy and the average particle size of the nanofibers was made through transmission electron microscopy. In H y HRFN the strain percent and compression resistance (Rc) were measured. The fique nanofibers showed diameter and length averages of 25.2 ± 6.2 nm and 483.8 ± 283.2 nm respectively. Maximum degradation temperature was 317 °C. HRFN presented higher compression resistance (16.39 ± 4.30 kPa) and this resistance was 2.5 greater than the resistance of H (6.49 ± 2.48 kPa). The results indicate that fique lignocellulosic matrix has potential application for obtaining polymeric type composite materials.