The La2/3Sr1/3MnO3 (LSMO) with Curie temperature above room temperature is the leading compound of the manganite perovskite family. Therefore, the physical properties are desirable for practical applications as magnetic sensors. However, when the dimensions are reduced the ferromagnetic properties of material are weakened. In this research, we have grown La2/3Sr1/3MnO3/SrTiO3 thin films by sputtering DC at high oxygen pressure at 830°C. X-Ray Diffraction (XRD) analysis reveals that only (0 0 2) LSMO peak are present, indicating a textured growth. The samples morphology was characterized by Atomic Force Microscopy (AFM). Additionally, LSMO microwires were patterned by UV lithography; the devices are a well-defined channel with current and voltage leads enabling four points resistance measurements. Resistivity versus temperature curves displays typical manganite behaviour with metal-insulator transition ∼350K. We study the electric and magnetotransport properties in LSMO film and in wire channel and their dependence with size (width and length) for potential applications like magnetic sensors.