Abstract This research presents the synthesis of novel nanocomposite ion exchange resins based on poly(sodium 4‐styrene sulfonate) and poly(2‐acrylamido glycolic acid). Nanocomposites were synthesized by in situ radical polymerization using organic modified montmorillonite as filler and different clay contents. Loaded resins showed improvements in mechanical properties compared with unloaded resins: specifically, when the nominal montmorillonite content was 2.5 wt%, poly(sodium 4‐styrene sulfonate) nanocomposite increased its shear modulus from 323 to 910 Pa and doubled its elastic recovery ratio, and the yield point was almost 20 times higher than for unloaded resins. In the case of metal ion retention, the effect of pH and clay content were studied for Cd(II), Pb(II), Cu(II), Cr(III) and Al(III) by a batch procedure. Results showed high efficiency, reaching over 80% after only 1 h of contact. Poly(2‐acrylamido glycolic acid) presented a higher pH dependence than poly(sodium 4‐styrene sulfonate). In addition, it was observed that montmorillonite contributes to retention capacity from the increase in distribution coefficients for loaded resins compared with unloaded resins. Copyright © 2011 Society of Chemical Industry