Aluminum-silicon coatings were deposited on stainless steel AISI 316 in the temperature range of 540 to 560°C by CVD-FBR. It was used a fluidized bed with 2.5% silicon and 7.5% aluminum powder and 90% inert (alumina). This bed was fluidized with Ar and as an activator a mixture of HCl/H2 in ratios of 1/10 to 1/16. Furthermore, the deposition time of the coatings was varied between 45 minutes to 1.5 hours, with a 50% active gas, neutral gases 50%. Thermodynamic simulation was conducted with the Thermocalc software to get the possible compositions and amount of material deposited for the chosen conditions. The coatings presented the follow compounds FeAl2Si, FeAl2 and Fe2Al5. Aluminum-silicon coatings were heat treated to improve its mechanical properties and its behavior against oxidation for the inter diffusion of the alloying elements. The heat treatment causes the aluminum diffuse into the substrate and the iron diffuse into coating surface. This leads to the transformation of the above compounds in FeAl, Al2FeSi, Cr3Si, AlFeNi and AlCrFe.