The crystal structure of the room temperature phase of MnIn2Te4, a material belonging to the II III2 VI4 family of semiconducting compounds, is examined using single crystal X-ray diffraction techniques as part of a systematic investigation of the cation ordering scheme in the (Cd1−xMnx)In2 Te4 system. The present study confirms that this material crystallizes in the tetragonal space group I42m (D, No. 121), with a = 0.6197(1) nm, c = 1.2402(2) nm, and Z = 2. The structure is a superstructure based upon a cubic close packed array of anions with the cations occupying a fraction of the available tetrahedral sites in a partially disordered fashion. The distribution of Mn/In over the cationic positions is determined by site-occupancy refinement. The refinement of the structure converges to the final disagreement factors R(F) = 0.0285 and Rw(F) = 0.0322 for all 188 independent reflections measured with a four-circle single-crystal diffractometer. Die Kristallstruktur der Raumtemperaturphase von MnIn2Te4, das zur II III2 VI4-Halbleiterfamilie gehört, wird mittels Einkristallröntgenbeugung im Rahmen einer systematischen Untersuchung der Kationenanordnung im Cd1−xMnxIn2 Te4-System ermittelt. Die tetragonale Raumgruppe I42m (D, No. 121) mit a = 0,6197(1) nm, c = 1,2402(2) nm und Z = 2 wird bestätigt. Die Struktur ist eine überstruktur auf der Grundlage einer kubisch dichten Packung von Anionen, in der die Kationen einen Teil der verfügbaren tetraedrischen Plätze in teilweise geordneter Weise einnehmen. Die Verteilung von Mn/In auf die Kationenplätze wird genau bestimmt. Die Strukturverfeinerung konvergiert gegen R(F) = 0,0285 und Rw(F) = 0,0322 für alle 188 unabhängigen Reflexe, die mit einem Vierkreis-Einkristalldiffraktometer gemessen werden.