This work shows a comparative analysis of geopolymers obtained by alkaline activation of two aluminosilicates: bentonite and metakaolin. With the goal of to replace some cement percentage, both aluminosilicates were added in several proportions (10, 20 and 30%) to concrete mixes. Portland Type I cement was used to prepare the reference concrete (without geopolymer). X-ray diffraction of geopolymers allowed to find new crystallographic phases that was not present in precursor's minerals. To evaluate mechanical properties of concrete prepared with geopolymers, test tubes with 7, 14, 28 and 90 days as setting time were used. Chemical resistance and Electrical impedance of concrete mixes were also measured. Results shows that cementitious material obtained from metakaolin exhibit the best compressive strength. On the other hand, those materials derived from bentonite, have a high electrical resistance so that, they protected reinforced concrete better that Portland does.