Polycrystalline samples of the semimagnetic semiconductor alloys (AgIn)1−zMn2zTe2 and (CuIn)1−zMn2zTe2 are used in lattice parameter, optical energy gap E0, and differential thermal analysis (DTA) measurements. The results indicate that in both, the zinc blende and chalcopyrite ranges of composition, ordering of the manganese can occur at lower temperatures, and a combination of the results is used to delineate the composition and temperature ranges in which disordered α and ordered α′ chalcopyrite and disordered ß and ordered β′ zinc blende is the equilibrium structure. It is shown that while the manganese ordering has little effect on the lattice parameter, it has appreciable effect on the values of E0. This is demonstrated by the different aiming points at z = 1.0 for the E0 vs. z lines in the different fields, the values being 2.8 eV for β, 1.95 eV for β′, and 1.35 eV for α′. Polykristalline Proben der semimagnetischen Halbleiterlegierungen (AgIn)1−zMn2zTe2 und (CuIn)1−zMn2zTe2 werden für Messungen der Gitterparameter, optischen Bandlücken E0 und differentiellen Thermoanalyse (DTA) benutzt. Die Ergebnisse zeigen, daß sowohl im Zinkblende- als auch im Chalkopyrit-Bereich der Zusammensetzung die Ordnung des Mangans bei tieferen Temperaturen auftritt, und eine Kombination der Ergebnisse wird benutzt, die Zusammensetzungs-und Temperaturbereiche zu zeichnen, in denen fehlgeordnetes α- und geordnetes α′-Chalkopyrit und fehlgeordnete β- und geordnete β′-Zinkblende die Gleichgewichtsstrukutren sind. Während der Manganordnungsprozeß nur einen geringen Einfluß auf den Gitterparameter hat, wird gezeigt, daß er einen wesentlichen Einfluß auf die Werte von E0 hat. Dies wird durch die verschiedenen Zielpunkte bei z = 1,0 für die E0–z-Linien in den verschiedenen Feldern demonstriert, wobei die Werte 2,8 eV für β, 1,95 eV für β′ und 1,35 eV für α′ betragen.