The T(z) phase diagram of the system CuIn1−zFezS2 is obtained from differential thermal analysis and X-ray diffraction measurements. It is found that the range of solid solution in the terminal chalcopyrite compounds at 200°C is limited to 0 < z < ≈ 0.20 for the CuInS2 α-phase and ≈ 0.94 < z < 1.0 for the CuFeS2 γ-phase. At higher temperatures, the cubic zinc-blende β-phase is found to extend across practically the whole composition range. Samples with 0.2 < z < 0.6, when rapidly quenched from the β field, show a metastable α-chalcopyrite condition, giving a useful extension of the composition range of the α-structure. At high values of z, the form of the diagram is complicated at higher temperatures by the dissociation of CuFeS2 into a zinc-blende phase β′ and pyrite. Aus Differentialthermoanalyse und Röntgenbeugungsmessungen wird das T(z)-Phasendiagramm des Systems CuIn1−zFezS2 erhalten. Es wird gefunden, daß der Bereich der festen Lösung in den Chalkopyrit-Endverbindungen bei 200°C auf 0 < z < ≈ 0,20 für die CuInS2-α-Phase und auf ≈ 0,94 < z < 1.0 für die CuFeS2-γ-Phase begrenzt ist. Es wird gefunden, daß sich die kubische Zinkblende-β-Phase bei höheren Temperaturen praktisch über den gesamten Zusammensetzungsbereich erstreckt. Bei schnellem Abschrecken vom β-Feld, zeigen Proben mit 0,2 < z < 0.6 einen metastabilen α-Chalkopyritzustand und ergeben eine nützliche Erweiterung des Zusammensetzungsbereichs der α-Struktur. Bei hohen Werten von z ist die Form des Diagramms bei höheren Temperaturen infolge der Dissoziation von CuFeS2 in eine Zinkblendenphase β′ und Pyrit komplizierter.